Product Description:
| Blanks Tolerance | +/-0.3~+/-2 mm |
| Forging Blank Size /Dimensions | 142 mm- 300mm or according to customer requirement |
| Blanks Weight | Max10000kg |
| Production Process for Forged parts | Forging, press, plus machining ,heat treatment , assembly |
| Applicable Machining Process | CNC Machining/ Lathing/ Milling/ Turning/ Boring/ Drilling/ Tapping/ Broaching/Reaming etc. |
| Carried Out Detection | Chemical Composition,Mechanical Properties,Non Destructive Testing,Size,Hardness. |
| Applicable Heat Treatment | Normalization , quenching and tempering, Case Hardening, Nitriding, Carbon Nitriding, Induction Quenching. |
1.7225 Steel can be used as forgings for aerospace, oil and natural gas, automobiles, agriculture and defense industry.
Chemical Composition(%)
| C | Si | Mn | Cr | Mo |
| 0.38-0.45 | 0.17-0.37 | 0.50-0.80 | 0.90-1.20 | 0.15-0.25 |
Mechanical Property
| Tensile Strength | Yield Strength | Elongation |
| 1150Mpa | 1050Mpa | 17.5% |
Product Description:
| Blanks Tolerance | +/-0.3~+/-2 mm |
| Forging Blank Size /Dimensions | 142 mm- 300mm or according to customer requirement |
| Blanks Weight | Max10000kg |
| Production Process for Forged parts | Forging, press, plus machining ,heat treatment , assembly |
| Applicable Machining Process | CNC Machining/ Lathing/ Milling/ Turning/ Boring/ Drilling/ Tapping/ Broaching/Reaming etc. |
| Carried Out Detection | Chemical Composition,Mechanical Properties,Non Destructive Testing,Size,Hardness. |
| Applicable Heat Treatment | Normalization , quenching and tempering, Case Hardening, Nitriding, Carbon Nitriding, Induction Quenching. |
1.7225 Steel can be used as forgings for aerospace, oil and natural gas, automobiles, agriculture and defense industry.
Chemical Composition(%)
| C | Si | Mn | Cr | Mo |
| 0.38-0.45 | 0.17-0.37 | 0.50-0.80 | 0.90-1.20 | 0.15-0.25 |
Mechanical Property
| Tensile Strength | Yield Strength | Elongation |
| 1150Mpa | 1050Mpa | 17.5% |