A forged blank is the result of this initial shaping process and typically has a simple and basic shape. It serves as a starting point for further machining and finishing operations to create a final product. Forged blanks are commonly used in industries such as automotive, aerospace, and manufacturing, where they can be further processed and machined into specific parts or components.
1CR11NI2W2MOV has good comprehensive mechanical properties. It has been widely used in the air industry to make important components such as engine blades, disks, and shafts that work below 600 ° C.
Chemical Composition(%)
| C | Si | Mn | P | S | Ni | Cr | Mo | W | V |
| 0.10-0.16 | ≦ 0.60 | ≦ 0.60 | ≦ 0.035 | ≦ 0.030 | 1.40-1.80 | 10.50-12.00 | 0.30-0.50 | 1.50-2.00 | 0.18-0.30 |
Mechanical Property
| Heat treatment | Mechanical properties ≧ | ||||||
| Qenching | Tempering | Tensile Strength （σb/MPa） | Yield Strength（σs/MPa） | Elongation （δ5/%） | Reduction ψ (%) | HRC | ak (J/㎡) |
1000-1020℃ Oil-quenched | 540-600℃ Air-cooled | 1080 | 885 | 12 | 50 | 33.5-41.5 | 685 |
A forged blank is the result of this initial shaping process and typically has a simple and basic shape. It serves as a starting point for further machining and finishing operations to create a final product. Forged blanks are commonly used in industries such as automotive, aerospace, and manufacturing, where they can be further processed and machined into specific parts or components.
1CR11NI2W2MOV has good comprehensive mechanical properties. It has been widely used in the air industry to make important components such as engine blades, disks, and shafts that work below 600 ° C.
Chemical Composition(%)
| C | Si | Mn | P | S | Ni | Cr | Mo | W | V |
| 0.10-0.16 | ≦ 0.60 | ≦ 0.60 | ≦ 0.035 | ≦ 0.030 | 1.40-1.80 | 10.50-12.00 | 0.30-0.50 | 1.50-2.00 | 0.18-0.30 |
Mechanical Property
| Heat treatment | Mechanical properties ≧ | ||||||
| Qenching | Tempering | Tensile Strength （σb/MPa） | Yield Strength（σs/MPa） | Elongation （δ5/%） | Reduction ψ (%) | HRC | ak (J/㎡) |
1000-1020℃ Oil-quenched | 540-600℃ Air-cooled | 1080 | 885 | 12 | 50 | 33.5-41.5 | 685 |