316L is a molybdenum-containing stainless steel. Due to the molybdenum in the steel, the overall performance of this steel is better than 310 and 304 stainless steel. Under high temperature conditions, when the concentration of sulfuric acid is lower than 15% or higher than 85%, 316L stainless steel has a wide range of properties. use. 316L stainless steel also has good resistance to chloride attack, so it is usually used in marine environments.
Chemical Composition(%)
C≤0.03
Si≤1.0
Mn≤2.00
P≤0.045
S≤0.030
Ni:10.0-14.0
Cr:16.0-18.0
Mo:2.0-3.0
Mechanical Property
Tensile Strength(Mpa) 485 MIN
Yield Strength(Mpa) 170 MIN
Elongation(%) 30 MIN
Reduction(%) 40 MIN
Hardness HRB<90 HV<200 HBS<187
316L is a molybdenum-containing stainless steel. Due to the molybdenum in the steel, the overall performance of this steel is better than 310 and 304 stainless steel. Under high temperature conditions, when the concentration of sulfuric acid is lower than 15% or higher than 85%, 316L stainless steel has a wide range of properties. use. 316L stainless steel also has good resistance to chloride attack, so it is usually used in marine environments.
Chemical Composition(%)
C≤0.03
Si≤1.0
Mn≤2.00
P≤0.045
S≤0.030
Ni:10.0-14.0
Cr:16.0-18.0
Mo:2.0-3.0
Mechanical Property
Tensile Strength(Mpa) 485 MIN
Yield Strength(Mpa) 170 MIN
Elongation(%) 30 MIN
Reduction(%) 40 MIN
Hardness HRB<90 HV<200 HBS<187